Koroziona otpornost 1.4713 vatrostalnog feritnog čelika u 0.5m nitratnoj kiselini

Naslov (eng)

Corrosion resistance of 1.4713 ferritic heat-resistant steel in 0.5M nitric acid

Autor

Dimitrijević, Stevan
Stevanović, Dimitrije
Dimitrijević, Silvana
Ivanović, Aleksandra
Cherkezova Zheleva, Zara
Kamberović, Željko

Opis (srp)

U ovom radu su predstavljena eksperimentalna istraživanja korozionog ponašanja i otpornosti feritnog (EN 1.4713/X10CrAlSi7) čelika u azotnoj kiselini koncentracije 0,50 moldm-3. Korozione karakteristike ovog čelika ispitane su sledećim elektrohemijskim metodama: potencijal otvorenog kola (POK), ekstrapolacija polarizacione krive u Tafelovom regionu i metoda linearnog polarizacionog otpora (LPO). Pored toga, korišćena je metoda gubitka mase (u trajanju od 10 dana) i upoređena je sa metodama polarizacije. Rezultati merenja pokazali su izvrsno međusobno slaganje elektrohemijskih metoda, sa razlikama u određenoj korozionoj struji u okviru ± 10%. Metoda gubitka mase pokazala je oko polovine vrednosti brzine korozije u odnosu na ove elektrohemijske metode. Iako izgleda kao značajna razlika, može se smatrati dobrim rezultatom, jer je to uobičajena razlika između ovih metoda; jer one određuju brzinu korozije u različito vreme izlaganja uzoraka u korozivnom okruženju. Opšti zaključak je da ispitivani nerđajući čelik otporan na visoke temperature ne pruža visoku otpornost na koroziju u 0,5M rastvoru azotne kiseline. Ovo istraživanje je izvedeno uzimajući u obzir procenu pogodnosti materijala za opremu za obnovljive izvore energije, poput baklji za odlagalište gasa (LGF) i dodatnu opremu tog sistema. Iako čelik 1.4713 ima dobre mehaničke i toplotne karakteristike, za upotrebu u takvim radnim uslovima potrebna je dodatna zaštita od korozije.

Opis (eng)

Experimental research of corrosion behavior and resistance of ferritic (EN 1.4713/X10CrAlSi7) steel in nitric acid with the concentration of 0.50 moldm-3 is presented in this paper. The corrosion characteristics of the steel were tested using the following electrochemical methods: open circuit potential (OCP), extrapolation of the polarization curve in the Tafel region, and linear polarization resistance (LPR). Additionally, the weight-loss method (with a duration of 10 days) was used and compared with the polarization methods. The measurement results have shown excellent agreement between electrochemical methods with the differences in determining corrosion current within ±10%. Although it looks like a significant difference, it can be considered a good result since that is the usual difference between these methods because they determine the corrosion rates at different times of the samples exposal in corrosion environment. The general conclusion is that examined heat-resistant stainless steel does not provide high corrosion resistance in the 0.5M nitric acid. This research was performed considering assessing the suitability of the material for renewable energy equipment like landfill gas flares (LGF) and additional equipment for that system. Although the 1.4713 steel has good mechanical and thermal characteristics, it requires additional corrosion protection for use in such working conditions.

Jezik

engleski

Datum

2021

Licenca

© All rights reserved

Predmet

Key words: Ferritic steel; Nitric Acid; Corrosion; Landfill gas flare.

Ključne reči: feritni čelilk; nitratna kiselina; korozija; baklja deponijskog gasa.